纤维金属层板低速冲击仿真
投稿时间:2017-07-22  修订日期:2017-09-06  点此下载全文
引用本文:蔡艳,张斌,李振友.纤维金属层板低速冲击仿真[J].计算机辅助工程,2017,26(6):59-65.
作者单位E-mail
蔡艳 南京科技职业学院 zbcy418@163.com 
张斌 南京科技职业学院 847433732@qq.com 
李振友 上海飞机制造有限公司 zhenyouli@outlook.com 
中文摘要:采用Johnson-Cook模型模拟铝层的力学行为,选用Hashin三维准则对复合材料层内损伤进行判断,采用Camanho-Matthews折减方案进行刚度折减,同时采用粘接元描述复合层板层间失效,采用Abaqus/Explicit结合VUMAT建立玻璃纤维增强铝合金层板冲击有限元模型。结果表明:随着冲击能量的变大,测量点的位移逐渐变大,钢球反弹后的测量点最大塑性变形也逐渐增大;纤维金属层板的玻璃纤维先发生破坏,然后铝合金层出现裂纹;2种层板的抗低速冲击性能基本相同。研究结果可用于玻璃纤维铝合金层板抗冲击性能的对比分析。
中文关键词:纤维金属层板  低速冲击  Hashin三维准则  Camanho Matthews折减  粘接元  损伤力学
 
Simulation on low velocity impact of fiber metal laminates
Abstract:The mechanical behavior of aluminum layer is simulated by Johnson-Cook model. The Hashin 3D criterion is used to judge the inner-layer damage of composite material layer. The Camanho-Matthews reduction scheme is used to reduce the stiffness, and the mortar element is used to describe the inter-layer failure of the composite laminates. The finite element model of the impact on the glass fiber reinforced aluminum alloy laminates is established by combining Abaqus/Explicit with VUMAT. The results show: with the increase of the impact energy, the displacement of the measuring point increases gradually, and the maximum plastic deformation of the measuring point increases gradually after the rebound of the steel ball; the glass fiber of fiber metal laminates is destroyed firstly, then the aluminum alloy layer cracks. The low velocity impact resistance of the 2 laminates is almost equal. The study results can be used for the comparative analysis of impact resistance of glass fiber reinforced aluminum laminates.
keywords:fiber metal laminate  low speed impact  Hashin 3D criterion  Camanho-Matthews reduction  mortar element  damage mechanics
查看全文  查看/发表评论  下载PDF阅读器

您是第5417821位访问者
地址:上海市浦东新区海港大道1550号上海海事大学图书馆B511 邮编:201306
联系电话:021-38284908 传真:021-38284916 E-mail:smucae@163.com
微信号:CAEChina   QQ:274226135   QQ群(中国CAE技术交流):204762677
本系统由北京勤云科技发展有限公司设计
沪ICP备11028865号-2